Engineering Composite Oxide SOFC Anodes for Efficient Oxidation of Methane

Ceramic anodes for solid oxide fuel cells SOFCs were prepared by aqueous impregnation of nitrate salts to produce composites with 45 wt % La0.8Sr0.2Cr0.5Mn0.5O3 LSCM in a 65% porous yttria-stabilized zirconia YSZ scaffold. Scanning electron micrographs indicate that the LSCM coats the YSZ pores following calcination at 1473 K. Composites produced in this manner exhibit conductivities at 1073 K of approximately 1 S/cm in air and 0.1 S/cm in humidified H2. A SOFC with a composite anode composed of 45 wt % LSCM, 0.5 wt % Pd, and 5 wt % ceria exhibited maximum power densities at 1073 K of 1.1 and 0.71 W cm-2 in humidified 3% H2O H2 and methane, respectively.